31221磁器貫入イエロー(1.8L) colored-underglazes *The black lines in the

*The black lines in the crazing (cracked) area of ​​the third sample plate are colored with ink

他にご注文の商品の製造に時間がかかる場合は、そちらに合わせた発送となります。

please discard the tap water approximately three days after using the glaze

dark place out of direct sunlight

vivid and reliable synthetic Gosu began to be widely used in Arita and across Japan

31221磁器貫入イエロー(1.8L) colored-underglazes *The black lines in the[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) Firing temperature : Reduction: 1280 Glazing : Baume concentration 50 (soak for about 3 seconds) [How to use] Soil type: porcelain, pottery Possible firing method: oxidation and reduction possible Appropriate firing temperature: 1230 1300 Baume